Front Bumper
EXTERIOR/INTERIOR TRIM
17 Sanding (III) Sand the coated surface and its surrounding areas using #400 sand paper and water.
18
Cleaning/
degreasing
Same as Process No. 12.
19 Top coat (I)
Non-colored Metallic paint
Use a “block” coating method.
•Recommended paint:
Suncryl (SC)
No. 307 Flex Hardener
SC Reducer (thinner)
•Mixture ratio:
Suncryl (SC) : No. 307 Flex Hardener = 3 : 1
•Viscosity: 11 — 13 sec./20°C (68°F)
•Coating film thickness: 40 — 50 µ
•Spraying pressure: 245 — 343 kPa
(2.5 — 3.5 kg/cm
2
, 36 — 50 psi)
Use a “block” coating method.
•Recommended paint:
Suncryl (SC)
No. 307 Flex Hardener
SC Reducer (thinner)
•Mixture ratio:
Suncryl (SC) : No. 307 Flex Hardener = 3 : 1
•Viscosity: 11 — 13 sec./20°C (68°F)
•Coating film thickness: 20 — 30 µ
•Spraying pressure: 245 — 343 kPa
(2.5 — 3.5 kg/cm
2
, 36 — 50 psi)
20 Leave unattended Not required.
Leave unattended at 20°C (68°F) for at least 10
minutes until the topcoat area is half-dry.
NOTE:
Be careful to keep dust or dirt from coming in
contact with the affected area.
21 Top coat (II) Not required.
Apply a clear coat three times at an interval of 3
to 5 minutes.
•Recommended paint:
SC710 Overlay Clear
No. 307 Flex Hardener
SC Reducer (thinner)
•Mixture ratio:
Suncryl (SC) : No. 307 Flex Hardener = 3 : 1
•Viscosity: 10 — 13 sec./20°C (68°F)
•Coating film thickness: 20 — 30 µ
•Spraying pressure: 245 — 343 kPa
(2.5 — 3.5 kg/cm
2
, 36 — 50 psi)
22 Drying
Allow the coated surface to dry for two hours at 20°C (68°F) or 30 minutes at 60°C (140°F).
NOTE:
Do not allow the temperature to exceed 80°C (176°F) since this will deform the PP substrate.
23 Inspection Carefully check the condition of the repaired area.
24
Removal of mask-
ing
Remove the masking tape applied in Process No. 11 and 13.
25 Parts installation Install parts on the bumper in reverse order of removal.
26
Bumper installa-
tion
Install the bumper.
Process
No.
Process name Job contents
asieps_tobira.book 27 ページ ２０１２年２月１０日 金曜日 午後３時２６分