Foundation: 2207, 2208 DIN 16932 German association for welding
Use for:
6100 / 6100 mobile / 6200 / 6111 / 6113 / 6113 mobile
1 bar on manometer: 173 N
PE 80 The value for heating element temperature is between 200° C - 220° C / 392 °F - 428 °F.
The smaller the pipe wall the higher the temperature.
PE 100 The standard value for heating element temperature is 220 °C / 428 °F.
Increase the change-over time and the welding pressure time at PE 100 as fast as possible !
time to
change- reach full
over welding cool-down time
0,15 (PE) time pressure
pressure in
T
desired
temperature
time
pipe pipe SDR bead-up circular heat-up max. time welding cool-
diameter wall pressure bead time change- to reach pressure down
OD (s) [bar] min. [s] over welding [bar] time
[mm] [mm] [mm] time pressure [min]
[s] [s]

bead-up heat-up
welding area
in welding area
Table for PE
Additional to the given bead-up force and to the welding force the moving force of the support must be added !
P (N/mm²)
630 15,4 41 26 2,0 154 9 9 26 20
630 19,3 33 33 2,5 193 10 11 33 24
630 24,1 26 40 2,5 241 11 13 40 30
630 30,0 21 50 3,0 300 16 16 50 37
630 35,7 17,6 58 3,0 357 13 18 58 43
630 37,4 17 61 3,5 374 16 23 61 45
630 46,3 13,6 74 3,5 463 19 19 74 56
630 57,2 11 90 4,0 572 22 29 90 67
630 70 9 107 4,0 700 25 35 107 80

Remaining under the cool-down time for up to 50% is allowed under the following conditions:
•
prefabrication under workshop conditions
•
low additional pressure at unclamping
•
no additional pressure during further cooling down
•
load onto the workpieces only after being completely cooled down
•
Join parts with wall thickness ≥15 mm
12.05.2015 Working Instructions WIDOS 6100 - 6200 Page 29 / 4 of 67