9 Fusion data
Operating instructions SG 160
44
Ø
Outside pipe diameter
e
Wall thickness
A
Fusion surface
F1
Equalization force
F2
Heating force
F5
Fusion force
S20
SDR 41
PN 2.5
Ø
32
40
50
63
75
90
110
125
140
160
e: wall thickness
mm
–
–
–
–
1,9
2,2
2.7
3.1
3.5
4.0
A: Fusion surface
mm²
–
–
–
–
436
607
910
1187
1500
1960
F1&F5 : fusion force
daN
–
–
–
–
4
6
9
12
15
20
Bead / Wulst / Bordino
mm
–
–
–
–
0.5
0.5
0.5
0.5
0.5
0.5
F2: heating force
daN
–
–
–
–
1
1
1
1
2
2
t2: heating time
sec
–
–
–
–
57
66
81
93
105
120
t3: change over time
sec
–
–
–
–
5
5
5
5
5
5
t4: Pressure buildup time
sec
–
–
–
–
6
6
6
6
6
6
t5: Cooling time
min
–
–
–
–
6
6
6
6
6
6
S 16
SDR 33
PN 3.2
Ø
32
40
50
63
75
90
110
125
140
160
e: wall thickness
mm
–
–
–
2,0
2,3
2,8
3.4
3.9
4.3
4.9
A: Fusion surface
mm²
–
–
–
383
525
767
1138
1484
1833
2387
F1&F5 : fusion force
daN
–
–
–
4
5
8
11
15
18
24
Bead / Wulst / Bordino
mm
–
–
–
0.5
0.5
0.5
0.5
0.5
0.5
0.5
F2: heating force
daN
–
–
–
1
1
1
1
1
2
2
t2: heating time
sec
–
–
–
60
69
84
102
117
129
143
t3: change over time
sec
–
–
–
5
5
5
5
5
5
5
t4: Pressure buildup time
sec
–
–
–
6
6
6
6
6
6
6
t5: Cooling time
min
–
–
–
6
6
6
6
6
6
7
S 12.5
SDR 26
PN 4
Ø
32
40
50
63
75
90
110
125
140
160
e: wall thickness
mm
–
–
–
2,5
2,9
3.5
4.2
4.8
5.4
6.2
A: Fusion surface
mm²
–
–
–
475
656
951
1396
1812
2283
2995
F1&F5 : fusion force
daN
–
–
–
5
7
10
14
18
23
30
Bead / Wulst / Bordino
mm
–
–
–
0.5
0.5
0.5
0.5
0.5
0.5
0.5
F2: heating force
daN
–
–
–
1
1
1
1
2
2
3
t2: heating time
sec
–
–
–
75
87
105
126
140
149
162
t3: change over time
sec
–
–
–
5
5
5
5
5
5
6
t4: Pressure buildup time
sec
–
–
–
6
6
6
6
6
6
7
t5: Cooling time
min
–
–
–
6
6
6
6
7
8
10