27
Effect:
If there is a top hole in the print model, you can increase this value
appropriately.
5.
Fill rate:
0 is hollow and 100 is solid.
Effect:
Decreasing fill can save printing time but affect the intensity. Hollows can
sometimes be caused by too thin wall thicknesses, cannot complete model printing.
proper filling is sometimes necessary.
6.
Print speed:
Recommended 40-60.
Effect:
Adjust the speed appropriately so that there is enough cooling time when
printing, and the model can print better.
7.
Printing temperature:
The temperature of the extrusion head when printing, ABS
recommended 210-230
℃
, PLA recommended 190-220
℃
.
Effect:
If the temperature is too low, it will not be able to be squeezed out and it will
get stuck and cause filament yielding incoherent.
8.
Hotbed temperature:
ABS recommended 90-100
℃
, PLA recommended 60-70
℃
.
Effect:
Too low temperature and not enough sticky filament will cause the stickiness
to be not tight and the appearance of an edge-up.
9.
Support type:
Because there will be overhang during printing, the filament might
drop for gravity reason. Therefore, a support is needed. but not for all.
None: No support
Touching buildplate: External support. Only add support for the overhang part, do not
add internal support.
Everywhere: Add to every part of the model as long as it is overhang, including inside
of the model.
Effect:
If the model is vacant, you need to add support. If you don't add support, the
printed filament will fall off if you hang it.
10.
Platform attachment type:
Adding a base allows the printed model to stick tighter.
None: No base is added. Brim: Thicken the base
and add attachments around it.
Raft: Mesh base.
Effect:
Adding a base can allow the platform to stick tighter, and a Raft type base can
save more material.
11.
Diameter:
Diameter of filament, the general diameter is 1.75mm.
12.
Flow:
The flow rate of the filament when printing.
Effect:
The two parameters of diameter and flow are used together. The larger the
diameter, the slower the filament output, The bigger rate of flow, the faster the
filament output.