TIG WELDING PARAMETERS
Stainless STEEL
Sheet
metal
thickness
mm.
Type of seam
Welding current (A)
Electrode
mm.
Filling
material
mm.
Welding
speed
mm./min.
Argon
lit./min.
Number
of
passages
Horizontal
position
Vertical
position
1
(.039 in)
Head to head 25
– 60
23
– 55
1.0 1.6 250
– 300
6 1
Overlapping 60 55 1.0 1.6 250
– 300
6 1
External angle 40 35 1.0 1.6 250
– 300
6 1
Internal angle 55 50 1.6 1.6 250
– 300
6 1
2
(.078 in)
Head to head 80
– 110
75
– 100
1.6
– 2.4
1.6
– 2.4
175
– 225
6 1
Overlapping 110 100 1.6
– 2.4
1.6 175
– 225
6 1
External angle 80 75 1.6
– 2.4
1.6 175
– 225
6 1
Internal angle 105 95 1.6
– 2.4
2.4 175
– 225
6 1
3
(.12 in)
Head to head 120
– 200 110 – 185
2.4
– 3.2
2.4 125
– 175
7 1
Overlapping 130 120 2.4
– 3.2
2.4 125
– 175
7 1
External angle 110 100 2.4
– 3.2
2.4 125
– 175
7 1
Internal angle 125 115 2.4
– 3.2
3.2 125
– 175
7 1
4
(.16 in)
Head to head 120
– 200 110 – 185
2.4
– 3.2
3.2 100
– 150
7 1
Overlapping 185 170 2.4
– 3.2
2.4 100
– 150
7 1
Internal angle 180 165 2.4
– 3.2
2.4
– 3.2
100
– 150
7 1
5
(.2 in)
External angle 160 140 3.2
– 4.0
2.4
– 3.2
100
– 150
7 1
6
(.24 in)
Head to head 220-275 190-230 3.2
– 4.0 3.00 – 4.00 150 - 240
7 2
Overlapping 250 - 300 210 - 250 3.2
– 4.0 3.00 – 4.00 150 - 240
7 2
Internal angle 280
– 320
230 - 280 3.2
– 4.0 3.00 – 4.00 150 - 240
7 2
COPPER and its alloys
Sheet
metal
thickness
mm.
Type of seam
Welding current
Horizontal position
(A)
Electrode
mm.
Filling
material
mm.
Welding
speed
mm./min.
Argon
lit./min.
Number
of
passages
1
(.04 in)
Head to head 70
– 90
1.6 1
– 1.6
300 6
– 8
1
Overlapping 70
– 100
1.6 1
– 1.6
300 7
– 8
1
Head 2 L 60
– 100
1.6 1
– 1.6
300 7
– 8
1
2
(.078 in)
Head to head 130
– 150
1.6 1.6 250 7
– 8
1
3
(.12 in)
Head to head 170
– 200
2.4
– 3.2
2.4
– 3.2
260 7
– 10
1 - 2
Internal angle 200
– 250
2.4
– 3.2
2.4
– 3.2
225 7 1
Overlapping 200
– 250
2.4
– 3.2
2.4
– 3.2
225 7
– 10
1
TIG welding parameters in direct current (DC).
Filling material
Filling material can be wire or rods; metal strips cut from the same weld piece metal can be used, in that case the
filling material must always be well cleaned.
The composition of the weld material must not generate porosity; it must be selected according to the basic
material to be worked on.
If suitable material is used, with uniform movement, the seam must be smooth, no porosities and look good.