36
The parameters listed here are standard values and may vary by up to +/- 20% in practice
due to factors relating to the join (magnetic fields, scale, etc.). Therefore, always carry out
a welding trial for borderline cases.
Sheet thickness:
from 3 mm
a-dimension single
layer:
a3 - a4.5
a3:
Vs-2 m/min
a4.5:
Vs-1.2 m/min
If an a-dimension greater than 4.5 mm is required, then multi-
layer technology is recommended.
Multiple layer fillet welds/PB position:
Sheet thickness:
from 3 mm
a-dimension multi
-
ple layer:
a3 - a4.5
Possible deposition rate: Up to 13.5 kg
Single layer edge welds/PA position:
Sheet thickness:
3 - 6 mm
Sheet thickness of 3
mm:
Vs-3.2 m/min
Sheet thickness of 6
mm:
Vs-1.8 m/min
Without pool support, 100% root formation is not possible.
Lap joints/PB position:
Sheet thickness (s): 1.5 - 2.5 mm
Sheet thickness of 2
mm:
Vs-3.3 m/min
Sheet thickness of
2.5 mm:
Vs-2.5 m/min
Lap joints/PB position:
Sheet thickness (s): 2.5 - 3.5 mm
Vs-2 - 2.5 m/min
Welding position as shown
Содержание Drive EasyTwin
Страница 2: ...2...
Страница 4: ...4...
Страница 8: ...8 Installing the CrashBox Drive EasyTwin on the robot 1 2 3 4 5 6 1 2 3 4 5 6...
Страница 12: ...12 3 Fully open 4 5 6 7 3 4 5 6 7...
Страница 13: ...13 EN 1 2 3 4 5 Set the contact pressure 3 rings must be visible 7 8 9 10 11...
Страница 14: ...14 6 7 12 13...
Страница 38: ...38 Replacing wearing parts Preparation replacing the feed rollers and nozzle 1 2 3 Fully open 4 5 6 1 2 3 4 5 6...
Страница 39: ...39 EN 7 8 9 10 11 12 7 8 9 10 11 12...
Страница 41: ...41 EN 5 6 Now the welding wire must be threaded see Threading the welding wire from Figure 5 on page 12 5 6...
Страница 42: ...42...
Страница 43: ...43 EN...