Kunststoffschweißtechnik
Foundation: 2207, 2208 DIN 16932 German association for welding
Use for:
Miniplast 2 / 110
OD 20 - 110
Maxiplast / 501 / 900 / 955
OD 50 - 160
Instaweld 160
OD 50 - 160
2000 / 3000 Kombi
OD 50 - 250
2500 DO 160 / 250 / 315
OD 50 - 315
ASM 160 / ASM 315
OD 50 - 315
PE 80
The value for heating element temperature is between 200° C - 220° C.
The
smaller
the pipe wall the
higher
the temperature.
PE 100
The standard value for heating element temperature is 220° C.
Increase the change-over time and the welding pressure time at PE 100 as fast as possible !
1 kp = 10 N
time to
change-
reach full
over welding
cool-down
time
0,15 (PE)
time
pressure
pressure in
T
desired
temperature
time
pipe
pipe
SDR
bead-up
circular
heat-up
max.
time
welding
cool-
diameter wall
force
bead
time
change-
to reach
force
down
OD
(s)
[kp]
min.
[s]
over
welding
[kp]
time
[mm]
[mm]
[daN]
[mm]
time
pressure [daN]
[min]
[s]
[s]
Table for PE
welding area
in welding area
Additional to the given bead-up force and to the welding force the moving force of the support must be added !
P (N/mm²)
bead-up
heat-up
280
6,9
41
89
1,0
69
6
6
89
10
280
8,6
33
110
1,5
86
7
7
110
12
280
10,7
26
136
1,5
107
7
7
136
14
280
13,4
21
169
2,0
134
8
9
169
18
280
15,9
17,6
198
2,0
159
9
10
198
20
280
16,6
17
207
2,0
166
9
10
207
21
280
20,6
13,6
252
2,5
206
10
12
252
26
280
25,4
11
305
2,5
254
12
14
305
31
280
31,3
9
367
3,0
313
14
16
367
38
280
38,3
7,4
437
3,5
383
16
20
437
47
315
7,7
41
112
1,5
77
6
6
112
11
315
9,7
33
140
1,5
97
7
7
140
13
315
12,1
26
173
2,0
121
8
8
173
16
315
15,0
21
213
2,0
150
9
9
213
19
315
17,9
17,6
251
2,0
179
10
11
251
23
315
18,7
17
262
2,0
187
10
11
262
24
315
23,2
13,6
320
2,5
232
11
13
320
29
315
28,6
11
386
3,0
286
13
15
386
35
315
35,2
9
465
3,0
352
15
18
465
43
315
43,1
7,4
553
3,5
431
18
22
553
52
Remaining under the cool-down time for up to 50% is allowed under the following conditions:
•
prefabrication under workshop conditions
•
low additional pressure at unclamping
•
no additional pressure during further cooling down
•
load onto the workpieces only after being completely cooled down
•
Join parts with wall thickness
≥
15 mm
14.04.2014
Working instructions WIDOS manual machine
page 22 / 8 of 42