Kunststoffschweißtechnik
Foundation: 2207, 2208 DIN 16932 German association for welding
Use for:
HRG 8 / 10 / 12 / 14 / 16
1 bar on manometer:
463
N
PE 80
The value for heating element temperature is between 200° C - 220° C.
The
smaller
the pipe wall the
higher
the temperature.
PE 100
The standard value for heating element temperature is 220° C.
Increase the change-over time and the welding pressure time at PE 100 as fast as possible !
time to
change-
reach full
over
welding
cool-down time
0,15 (PE)
time
pressure
pressure in
T
desired
temperature
time
pipe
pipe
SDR
bead-up
circular
heat-up
max.
time
welding
cool-
diameter wall
pressure bead
time
change-
to reach
pressure down
OD
(s)
[bar]
min.
[s]
over
welding
[bar]
time
[mm]
[mm]
[mm]
time
pressure
[min]
[s]
[s]
500
12,3
41
7
2,0
123
8
8
7
16
500
15,3
33
8
2,0
153
9
9
8
20
500
19,1
26
10
2,5
191
10
11
10
24
500
23,9
21,0
12
2,5
239
11
13
12
30
500
28,4
17,6
14
3,0
284
13
15
14
35
500
29,7
17
15
3,0
297
13
16
15
36
500
36,8
13,6
18
3,0
369
16
19
18
45
500
45,4
11
22
3,5
454
19
23
22
55
500
56
9
26
4,0
560
21
28
26
66
500
68,3
7,4
31
4,0
683
25
34
31
78
560
13,7
41
8
2,0
137
8
9
8
18
560
17,2
33
10
2,0
172
9
10
10
22
560
21,4
26
12
2,5
214
11
12
12
27
560
26,7
21
15
3,0
267
12
14
15
33
560
31,7
17,6
18
3,0
317
14
17
18
39
560
33,2
17
18
3,0
332
15
17
18
41
560
41,2
13,6
22
3,5
412
17
21
22
50
560
50,8
11
27
4,0
508
20
25
27
61
560
62,5
9
32
4,0
625
23
31
32
72
630
15,4
41
10
2,0
154
9
9
10
20
630
19,3
33
12
2,5
193
10
11
12
24
630
24,1
26
15
2,5
241
11
13
15
30
630
30,0
21
19
3,0
300
16
16
19
37
630
35,7
17,6
22
3,0
357
16
18
22
43
630
37,4
17
23
3,5
374
16
19
23
45
630
46,3
13,6
28
3,5
463
19
19
28
56
630
57,2
11
34
4,0
572
22
29
34
67
in welding area
Table for PE
bead-up
heat-up
Additional to the given bead-up force and to the welding force the moving force of the support must be added !
welding area
P (N/mm²)
26.04.2011
Working instructions WIDOS HRG 10
Page 26 / 1 of 49