The adhesion of glass build plate may decrease after long time using. Please apply proper amount of glue to keep and improve the adhesion.
Warping issues may occur when print ABS filament in cold environment, you may use glue to enhance the adhesion. It's not recommended to print ABS
filament at extremely low temperature environment, as print will fail when printed model getting away from the build plate.
There is a certain quivering on the build plate during the printing which may cause flatness changed. Thus please pay attention to the adhesion of the
first layer when printing model; if the distance of build plate and nozzle is improper, please re-level it.
If printing effect is not accurate enough, check the tension of synchronous belt and make it neither too loose nor too tight. When synchronous belt
working well, check the steps-per-mm under Settings. Turn up the steps-per-mm if the size gets smaller, or turns down the ratio if the size gets larger.
If the build plate or extruder kit shakes, use a wrench to adjust tightness of the pulley to the extent that the pulley cannot be rotated. Tightness is well
adjusted when slightly sliding the plate or extruder kit there gets no shaking.
If X-axis assembly shakes, adjust the distance between the pulley and the structural section properly using an open-end wrench; the pulley is well
adjusted when you cannot go on rotating it.
Optimal temperature for printing is 18~30℃. Too high or too low temperature is not good for printing results.
打印注意事项
玻璃平台长期使用后粘附力将有所下降，请适量涂抹胶水增加粘附力。
在低温环境中，打印ABS耗材容易发生翘边等异常情况，可涂抹胶水增强粘附力。不建议在温度过低的环境打印ABS材料，模型容易从平台脱离。
打印平台因在打印过程中可能存在抖动导致平面度发生变化。打印时请注意第一层的粘附是否正常；若不正常，请重新调平。
若打印成品在尺寸上有较大误差，请先确认同步带安装是否异常，是否太宽松或者过紧。若是，请调节至合适状态。若同步带无异常，可在设置中调节传动比：若成品尺寸偏
大，请调小传动比；若尺寸偏小，请调大传动比。
若发现平台或挤出组件有轻微晃动，请使用开口扳手适当调节滑轮的松紧度，使滑轮不可转动。当缓慢滑动平台或挤出组件时不再晃动，说明此时滑轮位置处于合适状态。
若发现X轴组件有晃动，请使用开口扳手适当调节滑轮与型材的距离。当用手拨动轮子不可转动时，说明此时滑轮位置处于合适状态。
建议打印环境温度为18-30℃，过高或过低的环境温度，都会影响打印质量。 1.
2.
3.
4.
5.
6.
7.