Instruction Manual

HMR

HMR-BA-e-1212

APPENDIX Table 1

Material

Method

Impact device

D/DC

D+15

Steel and cast steel

HRC

～

68.5

19.3

～

67.9

20.0

～

69.5

22.4

～

70.7

20.6

～

68.2

HRB

38.4

～

99.6

47.7

～

99.9

37.0

～

99.9

HRA

59.1

～

85.8

61.7

～

88.0

127

～

651

～

638

～

683

～

646

～

663

～

646

～

976

～

937

～

996

～

1042

～

950

32.2

～

99.5

33.3

～

99.3

31.8

～

102.1

35.8

～

102.6

30.6

～

96.8

Cold work tool steel

HRC

20.4

～

67.1

19.8

～

68.2

20.7

～

68.2

22.6

～

70.2

～

898

～

935

100

～

941

～

1009

Stainless steel

HRB

46.5

～

101.

～

655

～

802

Grey cast iron

HRC

～

334

～

326

Nodular cast iron

HRC

131

～

387

127

～

364

Cast

aluminium

alloys

～

164

～

210

～

168

HRB

23.8

～

84.6

22.7

～

85.0

23.8

～

85.5

BRASS (copper-zinc
alloys)

～

173

HRB

13.5

～

95.3

BRONZE

(copper-

alum./tin alloys)

～

290

Wrought

copper

alloys

～

315

Table 2

No.

Material

HLD

Strength σ

(MPa)

Mild steel

350

～

522

374

～

780

High-carbon steel

500

～

710

737

～

1670

Cr- Steel

500

～

730

707

～

1829

Cr-V Steel

500

～

750

704

～

1980

Cr-Ni Steel

500

～

750

763

～

2007

Cr-Mo Steel

500

～

738

721

～

1875

Cr-Ni-Mo Steel

540

～

738

844

～

1933

Cr-Mn-Si Steel

500

～

750

755

～

1993

Super strength steel

630

～

800

1180

～

2652

Stainless steel

500

～

710

703

～

1676

Содержание HMR

Страница 1: ...6 7 Memory Management 6 7 1 View from No 1 Group View from Ending Group 6 7 2 View from Selected No Group 6 7 3 Data Transfer 6 7 4 Delete by Group No 6 7 5 Delete all Data 6 7 6 Deletion Confirmation 6 8 Browsing Memory Data Groups 6 9 System Reset 6 9 1 LCD Brightness Setting 6 9 2 Date Time Setting 6 10 Software Information 6 11 System Calibration 6 12 EL Background Light 6 13 Auto Power Off 6 ...

Страница 2: ...able 1 1 No Item Qua ntity Remarks Stan dard Config uration 1 Main body 1 2 D type impact device 1 With cable 3 Standard test block 1 4 Cleaning brush I 1 5 Small support ring 1 6 Alkaline battery 4 AA size 7 Manual 1 8 Instrument case 1 9 Optio nal Config uration 11 Cleaning brush II 1 For use with G type impact device 12 Other type of impact devices and support rings Refer to Table 3 and Table 4...

Страница 3: ...RC HRA HV HS Display dot matrix LCD 128 x 64 dots Data memory max 500 groups Power supply 3V 2AA size Alkaline batteries Continuous working period about 50 hours with backlight off Communication interface USB1 1 4 Preparation Testing 4 1 Preparation and Inspection before Testing 4 1 1 Preparation of Sample Surface Preparation of the sample surface should conform to the relative requirements in APP...

Страница 4: ...b hardness tester and a corresponding hardness tester have to be used to test at the same sample respectively For each hardness value each homogeneous measurement 5 points of Leeb hardness value are needed They are in the surroundings of more than three indentations which need conversion of hardness The Leeb hardness arithmetic average value and the corresponding hardness average value as correlat...

Страница 5: ...he mean value will be displayed 6 3 3 Key Operation at the Main Display The SAVE key has to be pressed to store the present group of measured values into memory This operation is only valid after displaying the mean value The DEL key has to be pressed to delete the latest single measured value After pressing this key on the screen will be shown following The key or the key has to be pressed to mov...

Страница 6: ...ncel 6 5 2 Average Times Setting Average times can be modified within the range of 1 to 32 The 0 9 key has to be pressed to input the number value The cursor will shift right around automatically when inputting the number ETR has to be pressed to confirm ESC has to be pressed to cancel 6 5 3 Material Setting If Hard бb is preset to hardness following material will be displayed Steel and Cast Steel...

Страница 7: ...ceeds the measurement range the user will be reminded by the Tester to reset 2 If the bottom limit is larger than the upper limit they will be exchanged automatically 6 5 6 Hardness бb Setting ETR has to be pressed to switch between Hard and бb Note Only D and DC type of impact device have got the function of бb measurement So Hard is the only selection if the impact device is not D or DC type 6 6...

Страница 8: ...ssed to see details of that group The or key has to be pressed to browse details including average value test set and each single value ESC has to be pressed to return to previous display 6 9 System Set At the main display interface MENU key has to be pressed to enter the main menu or key has to be pressed to move the cursor to System Set Menu ETR has to be pressed to enter System Set Menu Auto Sa...

Страница 9: ... if it hasn t been used for a longer time or after having reset the system The key and the ETR key have to be pressed to power on the system Then the software calibration screen will display following The impact direction has to be set at 5 points have to be measured on the standard hardness block The average value will be displayed after measuring 5 times or key has to be pressed to input the nom...

Страница 10: ...e unscrewed first Then the impact body has to be taken out The nylon brush has to be spiralled in counter clock direction into the bottom of the guide tube It has to be taken out and repeated for 5 times At last the impact body and the support ring have to be installed again The impact body has to be released after use Any lubricant is absolutely prohibited inside the impact device 8 2 Normal Main...

Страница 11: ... 7 68 2 22 6 70 2 HV 80 898 80 935 100 941 82 1009 Stainless steel HRB 46 5 101 7 HB 85 655 HV 85 802 Grey cast iron HRC HB 93 334 92 326 HV Nodular cast iron HRC HB 131 387 127 364 HV Cast aluminium alloys HB 19 164 23 210 32 168 HRB 23 8 84 6 22 7 85 0 23 8 85 5 BRASS copper zinc alloys HB 40 173 HRB 13 5 95 3 BRONZE copper alum tin alloys HB 60 290 Wrought copper alloys HB 45 315 Table 2 No Mat...

Страница 12: ...1 6μm Min weight of sample Measure directly Need support firmly Need coupling tightly 5kg 2 5kg 0 05 2kg 5kg 2 5kg 0 05 2kg 1 5kg 0 5 1 5kg 0 02 0 5kg 15kg 5 15kg 0 5 5kg 5kg 2 5kg 0 05 2kg Min Thickness of sample Coupling tightly Min layer thickness for surface hardening 5mm 0 8mm 5mm 0 8mm 1mm 0 2mm 10mm 1 2mm 5mm 0 8mm Size of tip indentation Hardness 300HV Indentation diameter Depth of indenta...

Результаты поиска

Содержание HMR

Отзывы:

Похожие инструкции для HMR

Бренды по названию

Популярные бренды

sauter HMR, Инструкция по эксплуатации

Результаты поиска

Содержание HMR

Отзывы:

Похожие инструкции для HMR

Бренды по названию

Популярные бренды