TECHNICAL DATA SHEET
TECHNICAL DATA
Basic material : MS Polymer
Curing method : moisture
Specific density (20°C) : ca. 1.4 kg/liter
Skin forming time (20°C/50% R.H.) : ca. 12 min.
Open time (20°C/50%R.H.) : < 15 min.
Curing speed after 24 hrs (20°C/50%R.H.) : ca. 4 mm
Shore A hardness (DIN 53505) : ca. 55
Volume change (DIN 52451) : < 3%
Green strength (Physica Rheometer MC100) : ca. 700 Pa
(max. load which can be applied per m² uncured adhesive without sagging)
Tensile stress (100%) (DIN 53504/ISO 37) : ca. 1.7 MPa
Tensile stress at break (DIN 53504/ISO 37) : ca. 2.8 MPa
Elongation at break (DIN 53504/ISO 37) : ca. 210%
Shear stress (DIN 53283/ASTM D1002) : ca. 2.5 MPa
(Alu-Alu; adh. thickness 2mm; test speed 50 mm/min.)
Tear propagation (DIN 53515/ISO 34) : ca. 14 N/mm
(Type C, test speed 500 mm/min.)
Solvent percentage : 0%
Isocyanate percentage : 0%
Temperature resistance : - 40°C till +120°C
Temperature resistance (max. 20 minutes) : +180°C
Application temperature : +5°C till +35°C
UV- and weather resistance : excellent
Colours (standard) : white, black
Packaging : 290 ml cartridges, 600 ml bags, other packaging on request.
STORAGE STABILITY
Dekasyl MS-5 may be stored for 12 months in a closed (unopened) packaging in a dry place at temperatures
b5°C and +30°C (cartridges 18 months).
SAFETY PRECAUTIONS
No specific safety precautions required. Consult safety data sheet.
TRANSPORT CLASSIFICATION
Not applicable.
©Dekalin November, 2013