Establishing a Weld Setting
Once the consumable wire type, wire size
and shielding gas have been chosen, the two
variables that are adjusted in order to obtain
the desired weld setting are;
• Wirefeed speed,
• Welding arc voltage.
The Weld Settings Chart in Figures 6a, 6b,
and 6c can be used to preset the machine
for an approximate welding current. For any
voltage control settings, there is a range of
valid wire speed settings.
Wirefeed speed is adjusted by Knob in
Figure 1 (11). The wirefeed speed determines
the welding current; increasing the speed
increases the current, and decreasing it
decreases current.
The selected wirefeed speed must be
matched with sufficient arc voltage; a speed
increase requires an increase of arc voltage.
If the voltage is too low the wire will stub
and stutter, and there will not be a steady
arc. If the voltage is too high the arc will be
long with metal transfer occurring as a series
of large droplets.
The weld setting should be chosen to suit the
application and the thickness of the metal to
be welded. It is important to check that the
deposited weld provides sufficient strength
to suit the application.
A “good” weld will have the characteristics
illustrated in Figure 4. The weld has penetrated
into the parent metal, fusing the root of the
joint where the two plates meet, and the weld
blends smoothly into the side walls.
A “bad” weld is shown in Figure 5. The weld
has not penetrated the joint root, and there
is poor side wall fusion. This lack of fusion
would normally be corrected by increasing
the arc voltage, or by increasing both
wirefeed speed and arc voltage to achieve a
higher current weld setting.
Fig 4
“Good” Weld
Fig 5
“Bad” Weld