Handling and soldering
Page 52 of 68
3.3
Soldering
3.3.1
Soldering paste
Use of "N“ Clean" ”oldering paste is strongly recommended, as it does not require cleaning after the soldering
process has taken place. The paste listed in the example below meets these criteria.
Soldering Paste:
LFSOLDER TLF-206-93F (Tamura Kaken (UK) Ltd.)
Alloy specification:
Sn 95.5/ Ag 3.9/ Cu 0.6 (95.5% Tin/ 0.6 % Silver/ 0.6% Copper)
Melting Temperature: 216 - –21°C
Stencil Thickness:
150 µm for base boards
The final choice of the soldering paste depends on the approved manufacturing procedures.
The paste-mask geometry for applying soldering paste should meet the recommendations in section 2.5.1
The quality of the solder joints on the connectors (‖half vias‖) should meet the appropriate IPC
specification.
3.3.2
Reflow soldering
A convection type-soldering oven is strongly recommended
over the infrared type radiation oven.
Convection heated ovens allow precise control of the temperature and all parts will be heated up evenly,
regardless of material properties, thickness of components and surface color.
Consider the "I“C-7530 Guidelines for temperature profiling for mass soldering (reflow and wave)
processes, published 2001".”Preheat phase
Initial heating of component leads and balls. Residual humidity will be dried out. Please note that this preheat
phase will not replace prior baking procedures.
Temperature rise rate: 1 - –°C/s
If the temperature rise is too rapid in the preheat phase it may cause
excessive slumping.
Time: 60 – 120 seconds
If the preheat is insufficient, rather large solder balls tend to be
generated. Conversely, if performed excessively, fine balls and large
balls will be generated in clusters.
End Temperature: 150 - –00°C
If the temperature is too low, non-melting tends to be caused in
areas containing large heat capacity.
Heating/ Reflow phase
The temperature rises above the liquidus temperature of 216 - –21°C. Avoid a sudden rise in temperature as the
slump of the paste could become worse.
Limit time above 220°C liquidus temperature: 20 - –0s
Peak reflow temperature: 230 - –50°C
Cooling phase
A controlled cooling avoids negative metallurgical effects (solder becomes more brittle) of the solder and
possible mechanical tensions in the products. Controlled cooling helps to achieve bright solder fillets with a
good shape and low contact angle.
Temperature fall rate: max 3°C / s
To avoid falling off, the u-blox 5 GPS module should be placed on the topside of the motherboard
during soldering.