Tecnodue I.T.S. PT 630, Operating Manual

Page: 20 / 36

I.T.S. Ital Trade Services PT 630 Operating Manual
20 20 20 20
PT 630 - DVS 2207-1
Cyl. section cm
2 17,3
Welding range 315-630 mm
material PE80-100 SDR 11
D S T P1 bead P2 t 2 t 3 t 4 P5 t 5
DIAMETER WALL THICK. TEMP. BEAD FORMATION HEATING UP CHANGEOV. RAMP COOLING
mm mm °C bar mm bar sec sec sec bar min
315 28,6 203 22,3 3,0 0.. 1,5 286 0.. 13 15 22,3 35
355 32,3 202 28,4 3,0 0.. 1,9 323 0.. 14 17 28,4 39
400 36,4 201 36, 3,0 0.. 2,4 364 0.. 16 19 36, 44
450 40,9 201 45,6 3,5 0.. 3,0 409 0.. 17 21 45,6 50
500 45,5 200 56,3 3,5 0.. 3,8 455 0.. 19 23 56,3 55
560 50,9 200 70,6 4,0 0.. 4,7 509 0.. 20 25 70,6 61
630 57,3 200 89,3 4,0 0.. 6,0 573 0.. 22 29 89,3 67
PT 630 - DVS 2207-1
Cyl. section cm
2
17,3
Welding range 315-630 mm
material PE80-100 SDR 9
D S T P1 bead P2 t 2 t 3 t 4 P5 t 5
DIAMETER WALL THICK. TEMP. BEAD FORMATION HEATING UP CHANGEOV. RAMP COOLING
mm mm °C bar mm bar sec sec sec bar min
315 35,0 201 26,7 3,0 0.. 1,8 350 0.. 15 18 26,7 43
355 39,4 201 33,9 3,5 0.. 2,3 394 0.. 17 20 33,9 48
400 44,4 200 43, 3,5 0.. 2,9 444 0.. 18 22 43, 54
450 50,0 200 54,5 3,5 0.. 3,6 500 0.. 20 25 54,5 60
500 55,6 200 67,2 4,0 0.. 4,5 556 0.. 21 28 67,2 66
560 62,2 200 84,3 4,0 0.. 5,6 622 0.. 23 31 84,3 72
630 70,0 200 106,7 4,0 0.. 7,1 700 0.. 25 35 106,7 80
PT 630 - DVS 2207-1
Cyl. section cm
2
17,3
Welding range 315-450 mm
material PE80-100 SDR 7,4
D S T P1 bead P2 t 2 t 3 t 4 P5 t 5
DIAMETER WALL THICK. TEMP. BEAD FORMATION HEATING UP CHANGEOV. RAMP COOLING
mm mm °C bar mm bar sec sec sec bar min
315 42,6 201 31,6 3,5 0.. 2,1 426 0.. 18 22 31,6 51
355 48,0 200 40,1 3,5 0.. 2,7 480 0.. 19 24 40,1 58
400 54,1 200 50,9 4,0 0.. 3,4 541 0.. 21 27 50,9 64
450 60,8 200 64,4 4,0 0.. 4,3 608 0.. 23 30 64,4 71
Warning!: in case of PE100 welding, temperature T must be increased to 220°c