Tweco ARCMASTER 401S, Руководство по эксплуатации

Страница: 52 / 64

ARCMASTER 401S POWER SOURCE
Base Metal
Thickness
DC Current
for Mild
Steel
DC Current
for Stainless
Steel
Tungsten
Electrode
Diameter
Filler Rod
Diameter (if
required)
Argon Gas
Flow Rate
CFH
Joint Type
0.040”
1.0mm
35-45
40-50
20-30
25-35
0.040”
1.0mm
1/16”
1.6mm
11-15 Butt/Corner
Lap/Fillet
0.045”
1.2mm
45-55
50-60
30-45
35-50
0.040”
1.0mm
1/16”
1.6mm
11-15 Butt/Corner
Lap/Fillet
1/16”
1.6mm
60-70
70-90
40-60
50-70
1/16”
1.6mm
1/16”
1.6mm
15 Butt/Corner
Lap/Fillet
1/8”
3.2mm
80-100
90-115
65-85
90-110
1/16”
1.6mm
3/32”
2.4mm
15 Butt/Corner
Lap/Fillet
3/16”
4.8mm
115-135
140-165
100-125
125-150
3/32”
2.4mm
1/8”
3.2mm
21 Butt/Corner
Lap/Fillet
1/4”
6.4mm
160-175
170-200
135-160
160-180
1/8”
3.2mm
5/32”
4.0mm
21 Butt/Corner
Lap/Fillet
Table 4-6: Welding Rate
TIG Welding is generally regarded as a specialized process that requires operator competency. While many of the
principles outlined in the previous Arc Welding section are applicable a comprehensive outline of the TIG Welding
process is outside the scope of this Operating Manual. For further information please refer to www.tweco.com
or contact Tweco.
4.04 TIG (GTAW) Welding Problems
FAULT CAUSE REMEDY
1 Excessive bead build up or
poor penetration or poor
fusion at edges of weld.
Welding current is too
low
Increase weld current and/or faulty joint
preparation.
2 Weld bead too wide and
flat or undercut at edges
of weld or excessive burn
through.
Welding current is too
high
Decrease weld current.
3 Weld bead too small or
insufficient penetration or
ripples in bead are widely
spaced apart.
Travel speed too fast Reduce travel speed.
4 Weld bead too wide or
excessive bead build up or
excessive penetration in
butt joint.
Travel speed too slow Increase travel speed.
5 Uneven leg length in fillet
joint
Wrong placement of
filler rod
Re-position filler rod.
BASIC WELDING GUIDE 4-14 Manual 0-5345