Flux and Electrode Stabilizing Guide
After Exposure to Moisture a
Sufficient Time to affect Weld Quality
Type (AWS
)
Air Conditioned
Storage
Before Opening
Dry Rod
Oven Holding
After Opening
Recondition
Step 1
Rebake
Step 2
180
°
F
±
25
°
two hours
240
°
F
±
25
°
one hour
Standard
EXX10
EXX11
EXX12
EXX13
EXX20
EXX30
80
°
F
±
20
°
60%
±
10% RH
140
°
F
±
30
°
Three hour total
180
°
F
±
25
°
two hours
325
°
F
±
25
°
one hour
Iron
Powder
EXX14
EXX24
EXX27
90
°
F
±
20
°
50% RH max
140
°
F
±
30
°
Three hour total
180
°
F
±
25
°
two hours
700
°
F
±
100
°
one-half hour
Iron
Powder
-
Low
Hydrogen
EXX18
EXX28
90
°
F
±
20
°
50% RH max
400
°
F
±
50
°
Two & one-half hour total
180
°
F
±
25
°
two hours
600
°
F
±
100
°
one-half hour
Low
Hydrogen
EXX15
EXX16
90
°
F
±
20
°
50% RH max
400
°
F
±
50
°
Two & one-half hour total
180
°
F
±
25
°
two hours
700
°
F
±
100
°
one-half hour
Low
-
Hydrogen
High Tensile
EXXX15
EXXX16
90
°
F
±
20
°
50% RH max
400
°
F
±
50
°
Two & one-half hour total
180
°
F
±
25
°
one hour
350
°
F
±
50
°
one hour
Stainless
Inconel
Monel
Nickel
Brasses
Bronzes
Hard Surfacing
Special Alloys
90
°
F
±
20
°
50% RH max
225
°
F
±
50
°
Two hour total
Granulated
or
Agglomerated
Flux
90
°
F
±
20
°
50% RH max
240
°
F
±
50
°
Not required
700
°
F
±
100
°
∅
two hours
CONTACT YOUR ELECTRODE MANUFACTURER FOR SPECIFIC INFORMATION INVOLVING
CRITICAL OPERATIONS.
Electrode coating should not be exposed to the rebaking temperature without first having been reconditioned at a lower
temperature. Failure to observe this rule will result in breakdown of electrode coatings.
After rebake, lower temperature to
holding level
until reissue
.
Note: In the HTS
Stainless electrode
groups, and 15 & 16
type coatings, there can
be a greater difference
in the maximum
temperature
requirements for
rebaking than those
shown. This can be
handled by special
request to the particular
manufacturer involved.
IMPORTANT:
This table is offered as a
guide to proper storage
and oven holding
temperatures for the
most common electrodes
in use today. In
addition,
recondition/rebake
procedures for electrode
coatings that have been
exposed to moisture for
a sufficient period of
time to affect the weld
quality are included.
Good judgment and the
manufacturer’s
recommendations should
be your guide.