202 AC/DC INVERTER BASIC WELDING
BASIC WELDING GUIDE
4-4
Manual 0-5239
Place the work so that the direction of welding is across, rather than to or from, your body. The electrode
holder lead should be clear of any obstruction so that you can move your arm freely along as the electrode
burns down. If the lead is slung over your shoulder, it allows greater freedom of movement and takes a lot of
weight off your hand. Be sure the insulation on your cable and electrode holder is not faulty, otherwise you
are risking an electric shock.
Striking the Arc
Practice this on a piece of scrap plate before going on to more exacting work. You may at first experience
difficulty due to the tip of the electrode "sticking" to the work piece. This is caused by making too heavy a
contact with the work and failing to withdraw the electrode quickly enough. A low amperage will accentuate it.
This freezing-on of the tip may be overcome by scratching the electrode along the plate surface in the same
way as a match is struck. As soon as the arc is established, maintain a 1.6mm to 3.2mm gap between the
burning electrode end and the parent metal. Draw the electrode slowly along as it melts down.
Another difficulty you may meet is the tendency, after the arc is struck, to withdraw the electrode so far that
the arc is broken again. A little practice will soon remedy both of these faults.
Art # A-07696_AB
20°
1.6 mm (1/16”)
Figure 4-10: Striking an Arc
Arc Length
The securing of an arc length necessary to produce a neat weld soon becomes almost automatic. You will
find that a long arc produces more heat. A very long arc produces a crackling or spluttering noise and the
weld metal comes across in large, irregular blobs. The weld bead is flattened and spatter increases. A short
arc is essential if a high quality weld is to be obtained although if it is too short there is the danger of it being
blanketed by slag and the electrode tip being solidified in. If this should happen, give the electrode a quick
twist back over the weld to detach it.
Rate of Travel
After the arc is struck, your next concern is to maintain it, and this requires moving the electrode tip towards
the molten pool at the same rate as it is melting away. At the same time, the electrode has to move along the
plate to form a bead. The electrode is directed at the weld pool at about 20º from the vertical. The rate of travel
has to be adjusted so that a well-formed bead is produced.
If the travel is too fast, the bead will be narrow and strung out and may even be broken up into individual
globules. If the travel is too slow, the weld metal piles up and the bead will be too large.
Making Welded Joints
Having attained some skill in the handling of an electrode, you will be ready to go on to make up welded joints.
A. Butt Welds
Set up two plates with their edges parallel, as shown in Figure 4-11, allowing 1.6mm to 2.4mm gap between
them and tack weld at both ends. This is to prevent contraction stresses from the cooling weld metal
pulling the plates out of alignment. Plates thicker than 6.0mm should have their mating edges bevelled to
form a 70º to 90º included angle. This allows full penetration of the weld metal to the root.