E-2
TROUBLESHOOTING
E-2
V155-S
Observe all Safety Guidelines detailed throughout this manual
PROBLEMS
(SYMPTOMS)
POSSIBLE
CAUSE
RECOMMENDED
COURSE OF ACTION
Excessive spatter
Craters
Inclusions
Insufficient penetration
Sticking
Porosity
Cracks
1. Long arc
2. High current
1. Fast movement of the electrode
away from piece.
1. Poor cleanliness or distribution of
the Welding passes.
2. Improper movement of the elec-
trode.
1. High progression speed.
2. Welding current too low.
3. Narrow chamfering.
1. Arc too short.
2. Current too low.
1. Humidity in electrode.
2. Long arc.
1. Current too high.
2. Dirty materials.
3. Hydrogen in weld (present on
electrode coating).
If all recommended possible areas of
misadjustment have been checked
and the problem persists,
Contact
your local Lincoln Authorized Field
Service Facility.
PROBLEMS IN STICK WELDING
If for any reason you do not understand the test procedures or are unable to perform the tests/repairs safely, contact your
Local Lincoln Authorized Field Service Facility
for technical troubleshooting assistance before you proceed.