Slic3r

•

Small perimeters

- Meant for holes, islands and ﬁne details, a slower

speed here is recommended.

•

External perimeters

- A slightly slower value may ensure cleaner

surfaces.

•

Infill

- As fast as you can without compromising the integrity of the

ﬁll structure. Faster extrusions can break and result in weak spots.

•

Solid infill

- The bottom of the model, and any additional solid

layers is usually slightly slower than inﬁll but faster than perimeters.

•

Top solid infill

- Allow time for the extrusion to cleanly cover

the previous top layers and result in a tidy top surface. The last few
layers should have bridged the inﬁll structure nicely, preparing the
way for a neat ﬁnish.

•

Support material

- Generally support structures are quick and dirty,

and so long as the base is adequately supported they can be built as
quickly as they can.

•

Bridges

- Having the extrusion span distances depends on the

material and cooling. Going too slow will result in sagging, too fast
will result in broken strands. Experimentation is the key here, but
generally bridging runs slower than perimeters.

•

Gap fill

- Filling in small gaps results in the extruder quickly

oscillating and the resulting shaking and resonance could have a
detrimental aﬀect on the printer. A smaller value here can guard
against this. A setting of zero disables gap ﬁlling completely.

•

Travel

- As fast as your printer will allow in order to minimise ooze.

•

First layer speed

- As mentioned in subsection 2.3, the ﬁrst layer is

important to lay down correctly, and a slower pace helps enormously.
Setting a value of 50%, or even less, can really help.

Acceleration control

is an advanced setting allowing acceleration

settings for perimeters, inﬁll, bridge, as well as a default setting, to be
made. Deciding which values to set depends on the capabilities of the
machine. Any settings within the ﬁrmware may be a good starting point.

54

PROOF

«
...
54
55
56
57
58
...
»

Содержание TAZ 4

Страница 1: ...Content Type Standard Color Paper Type STCO19 Page Count 130 File type Internal PROOF...

Страница 2: ...P R O O F...

Страница 3: ...TAZ 4 User Manual Aleph Objects Inc P R O O F...

Страница 4: ...odify this document under the terms of the Creative Commons Attribution 4 0 International Public License CC BY SA 4 0 Published by Aleph Objects Inc 626 W 66th Street Loveland Colorado 80538 USA For m...

Страница 5: ...r Host Software 22 2 Slic3r 23 2 1 Introduction 24 2 2 Getting Slic3r 25 2 3 First Print 26 2 4 Simple Mode 43 2 5 Expert Mode 52 2 6 Con guration Organization 81 2 7 Repairing Models 83 2 8 Advanced...

Страница 6: ...lts 107 4 8 Hot End 108 4 9 Electronics 108 5 Advanced Usage 109 5 1 Intro 110 5 2 Changing nozzles 110 5 3 ABS Acetone Glue 111 5 4 Using 1 75mm lament 111 6 Hardware and Software Source Code 115 7 3...

Страница 7: ...loaded 41 2 13 Preferences 43 2 14 Simple Mode Print Settings 44 2 15 An example of insu cient top layers 45 2 16 Creating a vase from a solid model 46 2 17 An example of an object printed with suppor...

Страница 8: ...ons Printer Settings Tab General Note the two extruders de ned in the left hand pane 71 2 44 Multiple extruder options Printer Settings Tab Extruder 71 2 45 Plater with multiple lament options 72 2 46...

Страница 9: ...rocessing script to display Slic3r environment variables 91 2 63 Example post processing script to print each line to output 92 3 1 GLCD Info Screen 99 3 2 Main menu 101 3 3 Con guration Menu 103 3 4...

Страница 10: ...P R O O F...

Страница 11: ...WARNINGS Safety Information P R O O F...

Страница 12: ...h the extruder nozzle or heater block without rst turning o the hot end and allowing it to completely cool down The hot end can take up to 20 minutes to completely cool Never touch recently extruded p...

Страница 13: ...lectronics Electrostatic discharge can damage electronic components Ground yourself by touching a grounded source like the metal power supply housing or your computer case Age Warning For users under...

Страница 14: ...P R O O F...

Страница 15: ...3D Printer Software P R O O F...

Страница 16: ...section at LulzBot com support downloads You will also nd instructions there for installing each program onto your PC You can also nd downloads speci c to the TAZ 3D printer on the TAZ product page 1...

Страница 17: ...ation Plater allows you to arrange and combine several STL les into one More information on the other programs within the Printrun package can be found at https github com kliment Printrun Printrun ca...

Страница 18: ...n Pronterface by using the following command in a terminal python pronterface py Installing from source Using Git in a terminal issue the following command git clone https github com kliment Printrun...

Страница 19: ...un Figure 1 2 Printrun Printrun is used to control the printer from a computer It is divided into 4 main parts The buttons over the top are used to connect to the printer load les and start stop print...

Страница 20: ...tty usbserial USB ID The Port button will refresh the Port listing Once selected choose the default 115200 buad rate and press Connect Pronterface will open a connection to the printer and display rmw...

Страница 21: ...moved by hand Keep in mind that there is no positional feedback so if you move an axis you will need to re home in order to re establish the hot end s position mm min XY Z These settings control the...

Страница 22: ...on to home the Z axis or the Home All button at this time In a later step you will need to set the Z end stop trigger before homing Z X Y Z Axes Movement Controls Prior to moving the X Y or Z axis mak...

Страница 23: ...d below outputs millimeters as the unit by default FreeCAD Website http free cad sourceforge net Although still in development FreeCAD is a great free libre CAD application Containing a full GUI for b...

Страница 24: ...er Host Software OctoPrint Website http octoprint org Octoprint is a printer host that uses a web based interface to access and control the 3D printer Added web cam functionality allows for time lapse...

Страница 25: ...Slic3r P R O O F...

Страница 26: ...manual slic3r org Goals Philosophy Slic3r is an original project started in 2011 by Alessandro Ranellucci aka Sound who used his considerable knowledge of the Perl language to create a fast and easy t...

Страница 27: ...n 32 and 64 bit versions to match their system Slic3r Slic3r can be downloaded directly from http slic3r org download Pre compiled packages are available for Windows Mac OS X and Linux Windows and Lin...

Страница 28: ...ble click the downloaded dmg le an instance of Finder should open together with an icon of the Slic3r program Navigate to the Applications directory and drag and drop the Slic3r icon into it The dmg l...

Страница 29: ...ulzbot com support downloads For information on loading and export Slic3r pro les please see page 81 Note that the pre set pro les will only work correctly when Slic3r is in Expert mode The pre set pr...

Страница 30: ...are The con guration wizard asks a series of questions and creates a con guration for Slic3r to start with When using the pre set TAZ Slic3r pro les you do not need to complete the Con guration Wizard...

Страница 31: ...e gcode produced by Slic3r is tailored to particular types of rmware The rst step prompts for the rmware that the printer uses For the TAZ printer select RepRap Marlin Sprinter Figure 2 2 Con guration...

Страница 32: ...sure to measure from the lower left corner where the extruder nozzle rests when are the home position to the maximum distance the nozzle can travel in each direction Take into account that the X carri...

Страница 33: ...ame from a source without a diameter given then carefully measure the aperture as accurately as possible One way of determining nozzle size is to very slowly 1mm s extrude some lament into free air an...

Страница 34: ...lament used in FDM printers is sold as being either 3mm or 1 75mm this is only a general guide The diameter can vary between manufacturers and even between batches Therefore it is highly recommended...

Страница 35: ...tic materials will have a di erent range This is one parameter which you will want to ne tune when you start producing prints The optimal temperature can vary even between colors of the same material...

Страница 36: ...rature the value will depend on the material used A rule of thumb is that PLA requires 35 C 60 C and ABS requires 85 C Note One may choose to control the bed temperature manually from the printer cont...

Страница 37: ...2 3 FIRST PRINT At this stage the wizard is complete and the basic con guration is de ned Figure 2 8 Con guration Wizard End 35 P R O O F...

Страница 38: ...thumb an additonal 5 is recommended Lower speeds Slowing down the extruder for the rst layer reduces the forces applied to the molten material as it emerges reducing the chances of it being stretched...

Страница 39: ...h rst layer height technique recommended above with this one Setting the rst layer height to 0 35mm and the rst extrusion width to 200 would result in a nice fat extrusion 0 65mm wide Bed material Man...

Страница 40: ...community It is similar to the STL format Additive Manufacturing File Format AMF was developed in re sponse to the limited nature of the STL format In addition to describing the geometry of the 3D mo...

Страница 41: ...available one of which is Meshlab8 a comprehensive tool for viewing and working with 3D les Figure 2 9 Shapesmith online CAD tool Working with Plater Slic3r has a tool called Plater which allows one...

Страница 42: ...e below the traditional RepRap Minimug9 is loaded and is viewed from above The ring around the model is a skirt a single perimeter several millimeters away from the model which is extruded rst This is...

Страница 43: ...2 12 STL le loaded The model can be repositioned by dragging the representation of it on the left of the screen around the bed Note that the dimensions of the bed should match your printer as given du...

Страница 44: ...rrange or export the models Add Opens a le dialog to add a model to the plater as an alternative to dropping a le directly Delete Delete All Remove one or all models from the plater Autoarrange Attemp...

Страница 45: ...le Mode Simple Mode Slic3r has two modes of operation Simple and Expert These may be chosen from the Preferences window found under the File menu Figure 2 13 Preferences Simple mode o ers a reduced se...

Страница 46: ...previous one There are several factors that in uence how high each layer should be Desired resolution Lower layer height should result in prints with less noticeable ribs or bands as each layer is sm...

Страница 47: ...subsection of the perimeter is not printed correctly then the second perimeter will help cover it The upper and lowermost layers that sandwich the model are lled with a Solid layers pattern For the bo...

Страница 48: ...tic this would be a waste of material and take a long time Instead most models can be lled with less material which is then sandwiched between layers lled at 100 see Solid layers above A density value...

Страница 49: ...he support material is printed Figure 2 17 An example of an object printed with support material Tip It is sometimes worth considering altering the orientation of the model in order to possibly reduce...

Страница 50: ...rs to the rst layer as a base ange in order to provide more surface area for the print to stick to the bed with in order to reduce warping see 2 3 The brim is then cut away once the print is nished an...

Страница 51: ...lue should ideally be set in the rmware it can be useful to test slight changes to the rate by altering this value It varies the amount of plastic proportionally and should be changed in very small st...

Страница 52: ...round which the print will be centered A Bed size of 200mmx200mm and a Print center of 100mmx100mm would sit the print in the middle Should it be desired to print away from the center because of a scr...

Страница 53: ...rs before travel The retraction will then be compensated for by the same amount after the travel move before starting the new extrusion path A value of between 1 and 2mm is usually recommended Bowden...

Страница 54: ...which is that the results are produced quicker but also faster print times can be utilised in producing more layers i e lower layer height thus improving perceived print quality An additional bene t...

Страница 55: ...icated a value can be given in percentage This is in relation to the preceding value e g 50 solid in ll would be half of the value de ned for in ll A few general guidelines for each option Perimeters...

Страница 56: ...aving the extrusion span distances depends on the material and cooling Going too slow will result in sagging too fast will result in broken strands Experimentation is the key here but generally bridgi...

Страница 57: ...2 5 EXPERT MODE Take into account any restrictions enforced by the rmware as many have settings for the maximum safe speed of each axis 55 P R O O F...

Страница 58: ...In ll pattern settings Slic3r o ers several in ll patterns four regular and three more exotic avours The numbers given in brackets below each gure are a rough estimate of material used and time taken...

Страница 59: ...25 In ll pattern Concentric 351 80mm 5m 30s Figure 2 26 In ll pattern Honeycomb 362 73mm 5m 39s Figure 2 27 In ll pattern Hilbert Curve 332 82mm 5m 28s Figure 2 28 In ll pattern Archimedean Chords 333...

Страница 60: ...ach layer forming a strong vertical structure Figure 2 30 In ll pattern comparison in a complex object Left to Right honeycomb line Most models require only a low density in ll as providing more than...

Страница 61: ...5 EXPERT MODE Figure 2 31 In ll patterns at varying densities Left to Right 20 40 60 80 Top to Bottom Honeycomb Concentric Line Recti linear Hilbert Curve Archimedean Chords Octagram Spiral 59 P R O O...

Страница 62: ...terials Solid infill every n layers Forces a solid ll pattern on the speci ed layers Zero will disable this option Fill angle By default the in ll pattern runs at 45 to the model to provide the best a...

Страница 63: ...preferable as the perimeter acts as a wall containing the in ll Fighting Ooze Unless the material being extruded has a very high viscosity it will ooze from the nozzle in between extrusions There are...

Страница 64: ...l moves then it may be useful to add a small amount of additional material Minimum travel after retraction Triggering a retraction after very short moves is usually unnecessary as the amount of ooze i...

Страница 65: ...e the start point to a di erent location for each layer See also subsection Sequential Printing on page 84 for another tech nique which can minimise strings forming between objects Skirt The Skirt set...

Страница 66: ...ing print quality Too hot and the material deforms too cool and layer adhesion may be problematic Applying cooling will allow the freshly deposited material to solidify enough to provide a good base f...

Страница 67: ...not cool any heated bed more than necessary It should also not cool the heater block of the hot end so as not to force it to do more work and waste energy The air movement should aim for the nozzle ti...

Страница 68: ...detailed how important the rst layer is and so it makes sense not to apply the fan until sure the print is securely attached to the bed Keeping the fan turned o for the rst two or three layers is a g...

Страница 69: ...is determined by several factors most notably layer height and extrusion width and is usually around 45 For models with larger overhangs a support structure may have to be printed below it This incurs...

Страница 70: ...required Small models and those with small footprints can sometimes break or detach from the bed Therefore the Enforce support option will cause support structures to be printed for the given number o...

Страница 71: ...his attribute take into account the width of the support extrusion and the amount of support material that will adhere to the object Care should be taken to choose a support pattern which matches the...

Страница 72: ...ort or perimeters Multi material printing requires a suitably designed object usually written in AMF format as this can handle multiple materials see Model Formats in 2 3 Details on how to create such...

Страница 73: ...which are particular to multi extruder setups Figure 2 44 Multiple extruder options Printer Settings Tab Extruder The Extruder offset is to be used should the rmware not handle the displacement of ea...

Страница 74: ...Assigning Filaments When a printer pro le with multiple extruders has been selected the Plater tab allows the selection of a di erent lament for each extruder Figure 2 45 Plater with multiple lament o...

Страница 75: ...ion of the Printer Settings tab has an option for inserting G code between tool changes As with all custom G code subsections placeholder variables can be used to reference Slic3r settings This includ...

Страница 76: ...i material AMF le Split the original design into the separate parts within the CAD program and export each part as STL Within Slic3r choose Combine multi material STL files from the File menu When pro...

Страница 77: ...ere it may be bene cial to modify extrusion widths Perimeter A lower value will produce thinner extrusions which in turn will produce more accurate surfaces Infill and Solid Infill A thicker extrusion...

Страница 78: ...ns and other parts could be printed with a ner layer height for example sloping gradients where layering appears more pronounced The model in g 2 49 gives a rudimentary example of where variable layer...

Страница 79: ...ght The variable layer height options are available by double clicking on a part name in the Plater window This will cause a pop up window to be displayed which contains two tabs The rst gives some in...

Страница 80: ...52 presents a table where each row de nes a layer height for a particular range along the Z axis given in millimeters In this example the walls of the model are printed at 0 4mm the steeper parts of...

Страница 81: ...ODE Figure 2 52 Variable layer height options Layers The resulting G Code g 2 53 shows a higher de nition which should result in a higher quality print Figure 2 53 Example with variable layer height 7...

Страница 82: ...height An additional feature of the variable layers height option is that by entering a zero for a range that part of the model will not be printed Fig 2 55 shows the G Code where layers between 0 an...

Страница 83: ...ting as each minor change to a parameter may have to be duplicated across many con gurations For this reason pro les are a more suitable way of managing multiple con gurations This method also allows...

Страница 84: ...Slic3r Figure 2 56 Saving a pro le Pro les can be deleted by choosing the pro le to delete and clicking the red delete button next to the save button Figure 2 57 Deleting a pro le 82 P R O O F...

Страница 85: ...ribed here are all free at the time of writing FreeCAD Freecad16 is a comprehensive and free CAD program which comes with a mesh module in which repairs to degenerate models can be made The following...

Страница 86: ...for example by removing important triangles Export the repaired model via the Export menu option or context menu 2 8 Advanced Topics Sequential Printing When printing several objects at once it can be...

Страница 87: ...s The clearance that should be given around the extruder Take care if the extruder is not mounted centrally take the largest safe value Height The vertical distance between the nozzle tip and the X ax...

Страница 88: ...output gcode to by default the file will be saved into the same directory as the input file using the output filename format to generate the filename j threads num Number of threads to use 1 default...

Страница 89: ...ptions travel speed Speed of non print moves in mm s default 130 perimeter speed Speed of print moves for perimeters in mm s default 30 small perimeter speed Speed of print moves for small perimeters...

Страница 90: ...plied file default nothing toolchange gcode Load tool change G code from the supplied file default nothing extra perimeters Add more perimeters when needed default yes randomize start Randomize starti...

Страница 91: ...eed Maximum fan speed default 100 bridge fan speed Fan speed to use when bridging default 100 fan below layer time Enable fan if layer print time is below this approximate number of seconds default 60...

Страница 92: ...over layer height like 200 first layer extrusion width Set a different extrusion width for first layer perimeter extrusion width Set a different extrusion width for perimeters infill extrusion width S...

Страница 93: ...e G Code le that Slic3r generates All Slic3r con guration options are made available to the scripts by way of environment variables These all begin with SLIC3R_ The following script would write out al...

Страница 94: ...Slic3r usr bin perl i use strict use warnings while modify _ here before printing print Figure 2 63 Example post processing script to print each line to output 92 P R O O F...

Страница 95: ...ibbing you should always choose a layer height that is a multiple of your full step length To calculate the full step length for the screws you re using take the pitch of your screws I recommend M6 wi...

Страница 96: ...com alexrj Slic3r wiki FAQ Blog The Slic3r blog contains tips hints and advice http slic3r org blog IRC Found on the irc freenode net server the following chat rooms are often lled with people who ca...

Страница 97: ...ues Please take the time to read through the existing issues to see whether the problem has already been submitted Also make sure that the problem is a bug in the application do not submit support rel...

Страница 98: ...P R O O F...

Страница 99: ...Printing with the Graphic LCD P R O O F...

Страница 100: ...m calibration checks Because of this it is easier and faster to make the required manual movements within Printrun Calibration checks can be done with the Graphic LCD but require a number of repetitiv...

Страница 101: ...d gcode les drag and drop or paste the gcode les to the SD card Once the les have transferred eject the SD card from your computer and insert it back into the SD card slot on the left side of the Grap...

Страница 102: ...rdinates on the X Y and Z axes 5 Feed rate represents the current feed rate setting The feed rate is set to 100 by default this matches the speed set in the gcode generation When on the status screen...

Страница 103: ...on knob to bring up the menu and select Prepare Select Preheat PLA for PLA lament or Preheat ABS for ABS lament This will set the temperatures for the hot end and heat bed and begin bringing the print...

Страница 104: ...ing Manual Movements With the Graphic LCD As noted previously page 98 making numerous manual movements is easier done using the Printrun host software However you can make manual movements with the GL...

Страница 105: ...Among others these settings include default temperature settings and axis steps per millimeter The Store Memory and Load Memory functions will store and load the changes you make using the GLCD Contro...

Страница 106: ...Printing with the Graphic LCD GLCD Controller Menu Diagram Figure 3 4 Con guration Menu 104 P R O O F...

Страница 107: ...Maintaining Your 3D Printer P R O O F...

Страница 108: ...ch may compro mise the plastic parts Apply the silicone grease both above and below the X ends on the threaded rods and wipe down the threaded rods Use pronterface to drive the Z axis up and down to h...

Страница 109: ...he hardware in printing quality parts Each quarterly software update can bring advances in print quality The les are available at http download lulzbot com TAZ You can also nd updated software version...

Страница 110: ...he nozzle with acetone 4 9 Electronics The electronics case holding the RAMBo board may need dust blown out occasionally Power down the printer and use the provided 2 5 mm driver to remove the four M3...

Страница 111: ...Advanced Usage P R O O F...

Страница 112: ...ind if turned Heat the hot end to 160 C This will soften the plastic inside the hot end and allow the nozzle to be loosened o the threaded extension Power o the printer and once it cools continue unsc...

Страница 113: ...small amount to the wiping towel Acetone liquid and vapors are highly ammable Keep acetone away from open ames and high temperature sources including the 3D printer Read the warnings label on your pu...

Страница 114: ...nter and allow the hot end to cool Disconnect the two 4 pin connectors on the extruder assembly Locate and remove with the 2 5mm hex driver the tool head 3mm screw in top center of the X axis carriage...

Страница 115: ...these screws as you can crack the wooden plate 14 Wrap the wires through the strain relief slots in the correct path of all four wires snaking through each slot together 15 Place the hot end back dow...

Страница 116: ...P R O O F...

Страница 117: ...Hardware and Software Source Code P R O O F...

Страница 118: ...riginal source les 3D calibration objects and random novelties Production le for calculating large print runs Design les for all electronics and machined parts Budaschnozzle hot end RAMBo electronics...

Страница 119: ...3D Printer Support P R O O F...

Страница 120: ...ions or help The latest version of this information guide is also available at http download lulzbot com You can also nd more information including images videos and updated versions of this manual in...

Страница 121: ...Contact Information P R O O F...

Страница 122: ...com Phone 1 970 377 1111 x610 8 2 Sales Email sales LulzBot com Phone 1 970 377 1111 x600 8 3 Websites Aleph Objects Inc the makers of LulzBot 3D Printers www AlephObjects com LulzBot 3D Printers and...

Страница 123: ...zle 116 burns x bushings 106 C CAD 21 calibration 26 116 command line 86 community support 94 118 con guration export 81 import 81 Con guration Wizard 28 connecting 18 cooling 64 fans 65 slowing down...

Страница 124: ...hardware 116 hazards x heater block x 110 high resolution 110 hobbed bolt 107 Host 22 hot end 108 110 I in ll 56 60 IRC 94 118 L latex 116 layer height 76 license 25 lubricant 106 M maintenance 106 Ma...

Страница 125: ...eters 47 53 Small perimeters 53 Solid in ll 53 Support material 53 Top solid 53 Travel 47 53 Support material 47 Enforce support 67 Generate support material 47 67 Overhang threshold 67 Pattern 68 Pat...

Страница 126: ...07 116 Source Code 25 source code 116 speed 52 static xi STL 21 22 38 116 cleaning 42 stl 14 support material 67 T technical support 118 temperature x 14 64 threaded extension 110 threaded rods 106 U...

Страница 127: ...free speech not just free as in free beer although most free libre software is available for no cost Libre hardware designs can be copied modi ed and are usually available for download Free Libre soft...

Страница 128: ...eratures PET Polyethylene terephthalate PTFE Polytetra uoroethylene is a synthetic uoropolymer used in the Budaschnozzle for it s low coe cient of friction RAMBo R epRap A duino M ega compatible M oth...

Страница 129: ...P R O O F...

Страница 130: ...Colophon Created with 100 Free Libre Software GNU Linux L A TEX Memoir P R O O F...

Страница 131: ...P R O O F...

Страница 132: ...7IA9I9 dhiefb P R O O F...

Страница 133: ...P R O O F...

Отзывы:

Нет отзывов

Похожие инструкции для TAZ 4

Бренд: Canon Страницы: 86

Бренд: Canon Страницы: 20

Бренд: Chamjin I&C Страницы: 21

ExpressCard 2000

Бренд: Magtek Страницы: 25

Бренд: TallyGenicom Страницы: 310

Бренд: TallyGenicom Страницы: 330

Бренд: Oce Страницы: 12

Бренд: µ-Dimension Страницы: 74

Бренд: NEC Страницы: 10

Бренд: Oki Страницы: 189

Бренд: Zebra Страницы: 29

Бренд: MAC TOOLS Страницы: 2

Бренд: SII Страницы: 85

Бренд: SPRT Страницы: 18

Бренд: Canon Страницы: 32

Бренд: Canon Страницы: 162

Бренд: Canon Страницы: 170

Бренд: Canon Страницы: 184

Бренды по названию

0 1 2 3 4 5 6 7 8 9 A B C D E F G H I J K L M N O P Q R S T U V W X Y Z

Популярные бренды

Загрузить еще бренды