Table 6-5. Excessive Penetration
Good Penetration
Excessive Penetration − weld metal melt-
ing through base metal and hanging un-
derneath weld.
Excessive Penetration
Possible Causes
Corrective Actions
Excessive heat input.
Select lower amperage. Use smaller electrode.
Increase and/or maintain steady travel speed.
Table 6-6. Burn-Through
Burn-Through − weld metal melting com-
pletely through base metal resulting in
holes where no metal remains.
Possible Causes
Corrective Actions
Excessive heat input.
Select lower amperage. Use smaller electrode with lower amperage.
Increase and/or maintain steady travel speed.
Table 6-7. Waviness Of Bead
Waviness Of Bead − weld metal that is not
parallel and does not cover joint formed by
base metal.
Possible Causes
Corrective Actions
Unsteady hand.
Use two hands. Practice technique.
Table 6-8. Distortion
Distortion − contraction of weld metal dur-
ing welding that forces base metal to
move.
Base metal moves
in the direction of
the weld bead.
Possible Causes
Corrective Actions
Excessive heat input.
Use restraint (clamp) to hold base metal in position.
Make tack welds along joint before starting welding operation.
Select lower amperage for electrode.
Increase travel speed.
Weld in small segments and allow cooling between welds.
Summary of Contents for STICKMATE LX
Page 4: ......
Page 41: ...OM 316 Page 37 Return To Table Of Contents Notes ...
Page 44: ...OM 316 Page 40 Return To Table Of Contents Notes ...
Page 45: ......
Page 46: ......