Composition
1
Methacrylates
2 Initiators
3 Inhibitors
4 Dyes
Cured material
Post curing time using PCU EVO
10 min in a protective gas atmosphere
Flexural modulus ≥ 1700 MPa
Flexural strength ≥ 75 MPa
Elongation at break 10 - 15 %
Hardness 80 - 85 Shore D
8.2.3 FotoDent setup
FotoDent setup material is a 3D printing material suited for creating
orthodontic set-up models. FotoDent setup material has medical CE
approval.
The following table lists the material properties.
Characteristics
Colour
Maize yellow
Density
approx. 0.9 - 1.0 g/cm
3
Viscosity (23°C) 1.0 - 1.5 Pa s
Composition
1
Methacrylates
2 Urethane acrylates
3 Initiators
4 Pigments
5 Fumed silica
Cured material
Post curing time using PCU EVO
8 minutes with 80% LED-intensity
Flexural modulus ≥ 2000 MPa
Flexural strength ≥ 95 MPa
Elongation at break ≥ 5 %
Hardness approx. 80 - 85 Shore D
8.2.4 Resin handling notes
Each resin type has specific instructions for use. Refer to these instructions
for more information.
Shake the resin cartridge well to ensure an even mix of pigment.
Immediately clean up any spills using IPA (96%) or ethanol (96%). If left, the
resin cures, making cleaning more difficult.