Maintenance
Anti fouling Paints
Do not apply copper oxide based anti-fouling paints.
Do not paint over the anodes.
Anti-Seize Compounds
Do not use anti-seize compounds which are based on graphite, nickel or copper flakes -
these will cause corrosion.
Anti-seize compounds, usually containing zinc flakes, are available for aluminium.
Excessive wear:
If excessive wear or damage has been found, then undertake appropriate overhaul as described in the
overhaul section. Schedule the next maintenance period to suit the conditions found during this inspection,
using the following guidelines:

Decrease the time between each maintenance interval if the amount of dirt and sand in the water
increases.

Increase the time between each maintenance interval if amount of dirt and sand in water decreases.

Decrease interval if excessive wear was found in the jet unit internal inspection.

Increase interval if minimal wear was found at the jet unit internal inspection.
Control System
The control system must be regularly checked to ensure vessel safety. Thorough checks are recommended
every 30 hours.
Checking the steering system
Failure of certain components can cause loss of steering.
Make sure that the following components are regularly checked:

Security of the cable mounts and attachments.

Freedom of the steering shaft.

Security of the cotter pin.

Freedom of the steering nozzle.

Correct torque on the steering nozzle bolts.
Maintain the steering system in condition.
8-15