OPERATION
20
TIG of stainless steel (single run welding)
Workpiece
thickness
/mm
Joint
form
tungsten
electrode
diameter/mm
welding wire
diameter/mm
Argon gas
flow rate/
L
·
min
-1
welding
current
(DCEP)
Welding
speed/
cm
·
min
-1
0.8
Butt joint
1.0
1.6
5
20
～
50
66
1.0
Butt joint
1.6
1.6
5
50
～
80
56
1.5
Butt joint
1.6
1.6
7
65
～
105
30
1.5
Corner
joint
1.6
1.6
7
75
～
125
25
2.4
Butt joint
1.6
2.4
7
85
～
125
30
2.4
Corner
joint
1.6
2.4
7
95
～
135
25
3.2
Butt joint
1.6
2.4
7
100
～
135
30
3.2
Corner
joint
1.6
2.4
7
115
～
145
25
Notice: the above parameters originate from
《
Welding Dictionary
》
P150, Volume 1 of Edition 2.
§4.4.4 Electrode selection
The welding current reference for different electrode diameter
Electrode
diameter /mm
1.6
2.0
2.5
3.2
Parameters of piping back sealing welding for mild steel
（
DCEP
）
Piping
diameter
Φ
/mm
Tungsten
electrode
diameter/mm
Gas nozzle
diameter/mm
Welding
wire
diameter/mm
Welding
current/A
Arc
voltage/V
Argon
flow rate
/
L
·
min
-1
Welding
rate
/
cm
·
min
-1
38
2.0
8
2
75
～
90
11
～
13
6
～
8
4
～
5
42
2.0
8
2
75
～
95
11
～
13
6
～
8
4
～
5
60
2.0
8
2
75
～
100
11
～
13
7
～
9
4
～
5
76
2.5
8
～
10
2.5
80
～
105
14
～
16
8
～
10
4
～
5
108
2.5
8
～
10
2.5
90
～
110
14
～
16
9
～
11
5
～
6
133
2.5
8
～
10
2.5
90
～
115
14
～
16
10
～
12
5
～
6
159
2.5
8
～
10
2.5
95
～
120
14
～
16
11
～
13
5
～
6
219
2.5
8
～
10
2.5
100
～
120
14
～
16
12
～
14
5
～
6
273
2.5
8
～
10
2.5
110
～
125
14
～
16
12
～
14
5
～
6
325
2.5
8
～
10
2.5
120
～
140
14
～
16
12
～
14
5
～
6
Notice: the above parameters originate from
《
Welding Dictionary
》
P167, Volume 1 of Edition 2.